High Strength Industrial Silica Refractory Brick For Hot Blast Furnace / Coke Oven

Basic Information
Place of Origin: Zibo, China
Brand Name: Laurel
Certification: ISO9001
Model Number: Laurel-04-1
Minimum Order Quantity: 20ton
Packaging Details: packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages
Delivery Time: 20~30 days
Payment Terms: T/T;L/C
Supply Ability: 20,000 ton/Year
Product Name: Silica Insulation Refractory Shape:: Brick
Feature:: Acid Erosion Resistance Usage: Linings, Furnaces And Kilns Etc
Material:: Above 95% Silicon Oxide Temperature Range: Above 1650º C
High Light:

silica refractory brick

,

silicon carbide brick

 

High Strength Industrial Silica Refractory Brick For Hot Blast Furnace / Coke Oven

 

Description:
Our factory product various kinds of refractory products. The products can be made according with the customers' requirement.

Laurel can produces a large range of silica brick for many kind of industry usage.

SiO2 content: Above 95%.
Al2O3 content: Below 1.0%.
Usage: Hot-blast stove.

 

Features:

  1. Silicon oxide is above 95%.
  2. Good acid erosion resistance.
  3. High softening point with temperature.
  4. No shrink in burn repeatedly.
  5. Temperature of refractoriness under load is above 1650º C

 

Applications:

  1. Glass furnace
  2. Coke oven
  3. Blast furnace

 

Specifications:

Technical data

Silica brick for glass furnace

Item:

GF-96A

GF-96B

GF-95A

GF-95B

SiO 2

≥96

≥96

≥95

≥95

Fe 2 O 3

≤0.8

≤1.0

≤1.2

≤1.2

Apparent porosity %

≤22(24)

Cold Crushing

Strength MPa

Brick below20KG

≥35(30)

Brick ≥20KG

≥30(25)

Refractoriness under load ºC

≥1680

≥1670

≥1660

≥1650

True density g/cm ³

≤2.34

≤2.34

≤2.35

≤2.35

Silica brick for coke oven

Item:

CO-94A

CO-94B

SiO2: %

≥94

≥94

Al 2 O 3 : %

≤ 1.5

≤ 1.5

Fe2O3: %

≤ 1.5

≤ 1.5

Refractoriness under load 0.2Mpa

≥ 1650ºC

≥ 1650ºC

Apparent porosity: %

≤ 22

≤ 24

Bulk density: g/cm ³

≤ 2.34

≤ 2.35

Cold crushing strength: MPa

≥30

≥25

Permanent linear change % (1450ºC ×2h)

0~0.2

0~0.2

Thermal expansion(1000ºC)

≤1.28

≤1.30

Silica brick for hot blast furnace

Item

HBF-95

SiO2

≥ 95

Al2O3

≤ 1.0

Fe2O3

≤1.3

Apparent porosity %

≤22(24)

Cold crushing strength MPa

≥45(35)

Remaining quarts %

≤1.0

Refractoriness under load ºC

≥1650

Creep(0.2Mpa ×1550ºC×50h) %

≤0.8

Thermal expansion coefficient (1000ºC) %

≤1.25

Apparent density g/cm ³

≤2.32

 